简体中文 Materials for CNC Machining
| Material | Tensile Strength σb(Mpa) | Yield Strength σs(Mpa) | Hardness/HB | Densityg/cm3 | Elongation/% | Feature |
| 2024-T3/T4 | 470-485 | 325-345 | 120~145 | 2.82 | 10-12 | High strength High fatigue resistance |
| 5052-H32 | 228 | 193 | 60 | 2.68 | 12 | High strength High fatigue resistance |
| 6061-T6 | 310 | 275 | 95 | 2.73 | 6-10 | Good weldability Commonly extruded Suitable for hot forging |
| 6063-T5/T6 | 185 | 145 | 95 | 2.73 | 8 | Good weldability Commonly extruded Suitable for hot forging |
| 6082-T6 | 245 | 140 | 95 | 2.73 | 10 | Higher strength Lower ductility Wrought |
| 7075-T6 | 570 | 505 | 150 | 2.82 | 11 | Good fatigue strength Low resistance Good corrosion resistance High strength-to-density ratio |
| MIC-6 | 166 | 105 | 95 | 2.82 | 11 | Good corrosion resistant Good formability High intensity |
| Material | Tensile Strength σb(Mpa) | Yield Strength σs(Mpa) | Hardness/HB | Densityg/cm3 | Elongation/% | Feature |
|---|---|---|---|---|---|---|
| 1010 | 325 | 180 | 137 | 7.85 | 31 | Good plasticity Good toughness Low strength |
| 1018 | 453 | 245 | 197 | 7.85 | 14-22.5 | Good plasticity Good toughness Low strength |
| 1020 | 500 | 275 | 131 | 7.85 | 25 | Good plasticity Good toughness Low strength |
| A3 | 500 | 235 | 150 | 7.85 | 26.5 | Good combination property |
| A8 | 240 | 195 | 45-65 | 7.85 | 32 | High toughness High plasticity Low strength |
| A36 | 400 | 250 | 160 | 7.85 | 20 | Common welding material Cheap and easy on welding |
| 8620 | 1176 | 785 | 197 | 7.9 | 9 | High hardness High abrasive resistance High fatigue strength |
| 1045 | 625 | 530 | 229 | 7.85 | 16 | Good strength Low hardenability |
| 4130 | 560-731 | 460 | 229 | 7.85 | 12 | High strength Good hardenability Good toughness |
| 4140 | 1080 | 930 | 217 | 7.85 | 12 | High strength High hardenability Good toughness |
| 4340 | 745 | 470 | 269 | 7.85 | 12 | Excellent strength High fatigue strength Hign toughness |
| S7 | 680 | 650 | 215 | 7.85 | 10 | Good toughness Shock resistance High impact resistance |
| SKD-11 | 689 | 655 | 255 | 7.85 | 10 | High temperature strength High temperature resistance High hardness High wear resistant Good toughness Good hardenability High abrasive resistance |
| A2 | 689 | 655 | 248 | 7.85 | 10 | High abrasion resistance Excellent hardness High toughness |
| A10 | 335 | 205 | 137 | 7.85 | 12 | High abrasion resistance Excellent hardness Excellent toughness |
| D2 | 370 | 210 | 255 | 7.85 | 13 | High impact resistance High abrasive resistance |
| 8620 | 1176 | 785 | 261 | 7.85 | 9 | High temperature strength High temperature resistance High hardness |
| Material | Tensile Strength σb(Mpa) | Yield Strength σs(Mpa) | Hardness/HB | Densityg/cm3 | Elongation/% | Feature |
|---|---|---|---|---|---|---|
| 201 | 750 | 230 | 183 | 7.64-7.93 | 55-60 | Good acid/alkali-resisting High density Non-magnetic Pinhole-free |
| SS304 | 517 | 206 | 201 | 7.93 | 40 | Good combination property High corrosion resistance Good heat resistance High acid/alkali-resisting |
| 303 | 515 | 205 | 90-100 | 7.93 | 40 | High corrosion resistance High acid/alkali-resisting |
| 316 | 580 | 172 | 187 | 7.98 | 40 | High corrosion resistance High temperature resistance Excellent acid/alkali-resisting |
| 316L | 485 | 170 | 180 | 7.98 | 40 | High corrosion resistance High temperature resistance Excellent acid/alkali-resisting |
| 15-5PHSS | 550 | 200 | 187 | 7.93 | 40 | Good combination property High corrosion resistance Good heat resistance High acid/alkali-resisting |
| 17-4PHSS | 930 | 725 | 363 | 7.8 | 16 | High strength High corrosion resistance Excellent machinability |
| 17-7PHSS | 1030 | 725 | 380 | 7.93 | 16 | High strength Excellent corrosion resistance Good toughness |
| 440C | 560 | 250 | 269 | 7.75 | 20 | Excellent corrosion resistance High temperature resistance High hardness |
| 420 | 635 | 440 | 201 | 7.75 | 20 | Excellent corrosion resistance High temperature resistance High hardness |
| Material | Tensile Strength σb(Mpa) | Yield Strength σs(Mpa) | Hardness/HB | Densityg/cm3 | Elongation/% | Feature |
|---|---|---|---|---|---|---|
| Titanium Ti 6Al-4V | 235 | 140 | 195 | 4.51 | 50-60 | Low density Hign strength Resistant to corrosion in sea Water, aqua regia, and chlorine. |
| Titanium Grade 5 6Al-4V | 1050 | 827 | 195 | 4.5 | 25 | High tensile strength and toughness Light in weight Extraordinary corrosion resistance The ability to withstand extreme temperatures |
| Zamark#3 | 283 | 221 | 65-145 | 6.6 | 10 | Superior corrosion resistance Low creep strength |
| Bronze | 255 | 69 | 55-70 | 7.5-8.9 | 46-70 | Ductile High electrical conductivity |
| Brass | 478 | 239 | 53-56 | 8.5-8.8 | 44-60 | High electrical conductivity High malleability Good flow characteristics |
| Copper | 394 | 258 | 35-45 | 8.89 | 45-50 | Thermal High electrical conductivity High ductility |
| Material | Tensile Strength σb(Mpa) | Yield Strength σs(Mpa) | Hardness/HB | Densityg/cm3 | Elongation/% | Feature |
| 2024-T3/T4 | 470-485 | 325-345 | 120~145 | 2.82 | 10-12 | High strength High fatigue resistance |
| 5052-H32 | 228 | 193 | 60 | 2.68 | 12 | High strength High fatigue resistance |
| 6061-T6 | 310 | 275 | 95 | 2.73 | 6-10 | Good weldability Commonly extruded Suitable for hot forging |
| 6063-T5/T6 | 185 | 145 | 95 | 2.73 | 8 | Good weldability Commonly extruded Suitable for hot forging |
| 6082-T6 | 245 | 140 | 95 | 2.73 | 10 | Higher strength Lower ductility Wrought |
| 7075-T6 | 570 | 505 | 150 | 2.82 | 11 | Good fatigue strength Low resistance Good corrosion resistance High strength-to-density ratio |
| MIC-6 | 166 | 105 | 95 | 2.82 | 11 | Good corrosion resistant Good formability High intensity |
| Material | Tensile Strength σb(Mpa) | Yield Strength σs(Mpa) | Hardness/HB | Densityg/cm3 | Elongation/% | Feature |
|---|---|---|---|---|---|---|
| 1010 | 325 | 180 | 137 | 7.85 | 31 | Good plasticity Good toughness Low strength |
| 1018 | 453 | 245 | 197 | 7.85 | 14-22.5 | Good plasticity Good toughness Low strength |
| 1020 | 500 | 275 | 131 | 7.85 | 25 | Good plasticity Good toughness Low strength |
| A3 | 500 | 235 | 150 | 7.85 | 26.5 | Good combination property |
| A8 | 240 | 195 | 45-65 | 7.85 | 32 | High toughness High plasticity Low strength |
| A36 | 400 | 250 | 160 | 7.85 | 20 | Common welding material Cheap and easy on welding |
| 8620 | 1176 | 785 | 197 | 7.9 | 9 | High hardness High abrasive resistance High fatigue strength |
| 1045 | 625 | 530 | 229 | 7.85 | 16 | Good strength Low hardenability |
| 4130 | 560-731 | 460 | 229 | 7.85 | 12 | High strength Good hardenability Good toughness |
| 4140 | 1080 | 930 | 217 | 7.85 | 12 | High strength High hardenability Good toughness |
| 4340 | 745 | 470 | 269 | 7.85 | 12 | Excellent strength High fatigue strength Hign toughness |
| S7 | 680 | 650 | 215 | 7.85 | 10 | Good toughness Shock resistance High impact resistance |
| SKD-11 | 689 | 655 | 255 | 7.85 | 10 | High temperature strength High temperature resistance High hardness High wear resistant Good toughness Good hardenability High abrasive resistance |
| A2 | 689 | 655 | 248 | 7.85 | 10 | High abrasion resistance Excellent hardness High toughness |
| A10 | 335 | 205 | 137 | 7.85 | 12 | High abrasion resistance Excellent hardness Excellent toughness |
| D2 | 370 | 210 | 255 | 7.85 | 13 | High impact resistance High abrasive resistance |
| 8620 | 1176 | 785 | 261 | 7.85 | 9 | High temperature strength High temperature resistance High hardness |
| Material | Tensile Strength σb(Mpa) | Yield Strength σs(Mpa) | Hardness/HB | Densityg/cm3 | Elongation/% | Feature |
|---|---|---|---|---|---|---|
| 201 | 750 | 230 | 183 | 7.64-7.93 | 55-60 | Good acid/alkali-resisting High density Non-magnetic Pinhole-free |
| SS304 | 517 | 206 | 201 | 7.93 | 40 | Good combination property High corrosion resistance Good heat resistance High acid/alkali-resisting |
| 303 | 515 | 205 | 90-100 | 7.93 | 40 | High corrosion resistance High acid/alkali-resisting |
| 316 | 580 | 172 | 187 | 7.98 | 40 | High corrosion resistance High temperature resistance Excellent acid/alkali-resisting |
| 316L | 485 | 170 | 180 | 7.98 | 40 | High corrosion resistance High temperature resistance Excellent acid/alkali-resisting |
| 15-5PHSS | 550 | 200 | 187 | 7.93 | 40 | Good combination property High corrosion resistance Good heat resistance High acid/alkali-resisting |
| 17-4PHSS | 930 | 725 | 363 | 7.8 | 16 | High strength High corrosion resistance Excellent machinability |
| 17-7PHSS | 1030 | 725 | 380 | 7.93 | 16 | High strength Excellent corrosion resistance Good toughness |
| 440C | 560 | 250 | 269 | 7.75 | 20 | Excellent corrosion resistance High temperature resistance High hardness |
| 420 | 635 | 440 | 201 | 7.75 | 20 | Excellent corrosion resistance High temperature resistance High hardness |
| Material | Tensile Strength σb(Mpa) | Yield Strength σs(Mpa) | Hardness/HB | Densityg/cm3 | Elongation/% | Feature |
|---|---|---|---|---|---|---|
| Titanium Ti 6Al-4V | 235 | 140 | 195 | 4.51 | 50-60 | Low density Hign strength Resistant to corrosion in sea Water, aqua regia, and chlorine. |
| Titanium Grade 5 6Al-4V | 1050 | 827 | 195 | 4.5 | 25 | High tensile strength and toughness Light in weight Extraordinary corrosion resistance The ability to withstand extreme temperatures |
| Zamark#3 | 283 | 221 | 65-145 | 6.6 | 10 | Superior corrosion resistance Low creep strength |
| Bronze | 255 | 69 | 55-70 | 7.5-8.9 | 46-70 | Ductile High electrical conductivity |
| Brass | 478 | 239 | 53-56 | 8.5-8.8 | 44-60 | High electrical conductivity High malleability Good flow characteristics |
| Copper | 394 | 258 | 35-45 | 8.89 | 45-50 | Thermal High electrical conductivity High ductility |
Let's start a project today!
24/7 Engineering Support.
A quick & attractive quote within 6 hours.